Differences Between 52100 & E52100 Steel

AISI 52100

AISI 52100 alloy steel is known as a high carbon, chromium containing low alloy steel. The following datasheet gives an overview of AISI 52100 alloy steel.

E52100 Steel

AISI/SAE 52100 (UNS G52986) High-Carbon, Chromium Alloy
Typical Analysis
C Mn P S Si Cr
.98/1.10 .25/45 .025 Max .025 Max .15/.30 .1.3/1.6
Characteristics
  • This high carbon, chromium alloy is stocked in the annealed condition.
  • This grade is manufactured by the electric furnace process. Typically the quenched hardness is 62 to 66 HRC depending mainly upon section thickness
Typical Applications
  • Grade E52100 is used primarily for races and balls or rollers of rolling-element (anti-friction) bearings. The grade is also suitable for parts requiring high hardness and wear resistance
Typical Mechanical Properties (Annealed)
  • Yield - 85,000 psi
  • Tensile - 105,000 psi
  • Elongation - 17%
  • Reduction Area - 50%
  • BHN at surface - 228

52100 Chemical Composition

The following table shows the chemical composition of AISI 52100 alloy steel.

Element Content (%)
Iron, Fe 96.5 - 97.32
Chromium, Cr 1.30 - 1.60
Carbon, C 0.980 - 1.10
Manganese, Mn 0.250 - 0.450
Silicon, Si 0.150 - 0.300
Sulfur, S ≤ 0.0250
Phosphorous, P ≤ 0.0250

52100 Physical Properties

The physical properties of AISI 52100 alloy steel are listed in the following table.

Properties Metric Imperial
Density 7.81 g/cm3 0.282 lb/in³
Melting point 1424°C 2595°F

52100 Mechanical properties

The mechanical properties of AISI 52100 alloy steel are outlined in the following table.

Properties Metric Imperial
Bulk modulus (typical for steel) 140 GPa 20300 ksi
Shear modulus (typical for steel) 80 GPa 11600 ksi
Elastic modulus 190-210 GPa 27557-30458 ksi
Poisson's ratio 0.27-0.30 0.27-0.30
Hardness, Brinell - -
Hardness, Knoop (converted from Rockwell C hardness) 875 875
Hardness, Rockwell C (quenched in oil from 150°C tempered) 62 62
Hardness, Rockwell C (quenched in water from 150°C tempered) 64 64
Hardness, Rockwell C (quenched in oil) 64 64
Hardness, Rockwell C (quenched in water) 66 66
Hardness, Vickers (converted from Rockwell C hardness) 848 848
Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel) 40 40

52100 Thermal Properties

The thermal properties of AISI 52100 alloy steel are given in the following table.

Properties Metric Imperial
Thermal expansion co-efficient (@ 23-280°C/73.4- 36°F, annealed) 11.9 µm/m°C 6.61 µin/in°F
Thermal conductivity (typical steel) 46.6 W/mK 323 BTU in/hr.ft².°F

52100 SteelFabrication and Heat Treatment

52100 Steel Machinability

AISI 52100 alloy steel can be machined using conventional techniques. The machinability of this steel can be improved by performing spherodizing annealing process at 649°C (1200°F) before machining.

52100 Steel Forming

AISI 52100 alloy steel can be formed using all conventional techniques such as cold forging or stamping and hot or cold upset forming techniques.

52100 Steel Heat Treatment

AISI 52100 alloy steel is heated at 816°C (1500°F) followed by quenching in oil. Before performing this process, it is subjected to normalizing heat treatment at 872°C (1600°F) followed by slowly cooling in order to reduce the machining stress.

52100 Steel Forging

AISI 52100 alloy steel is forged at 927 to 1205°C (1700 to 2200°F).

52100 Steel Hot Working

AISI 52100 alloy steel can be hot worked at 205 to 538°C (400 to 1000°F).

52100 Steel Cold Working

AISI 52100 alloy steel can be cold worked using conventional techniques in the annealed or normalized conditions.

52100 Steel Annealing

For spheroidize anneale, the following isothermal anneal is recommended:

  • 1500ºF (815ºC) for 3 hours
  • 1350ºF (735ºC) for 4 hours
  • 1250ºF (675ºC) for 3 hours
  • Slow cool to 1000ºF (540ºC) then air cool.

52100 Steel Hardening

AISI 52100 alloy steel is hardened by cold working, or heating and quenching. It can be carburized at 913°C (1675°F) followed by quenching. It is again heated at 788°C (1450°F) followed by quenching for the second time.

52100 Steel Applications

AISI 52100 alloy steel is used in bearings in rotating machinery.

Chemical Composition of 52100 Bearing Steel and Equivalents

Standard Grade C Mn P S Si Ni Cr Cu Mo
ASTM A295 52100 0.93-1.05 0.25-0.45 0.025 0.015 0.15-0.35 0.25 1.35-1.60 0.30 0.10
DIN 17230 100Cr6/1.3505 0.90-1.05 0.25-0.45 0.030 0.025 0.15-0.35 0.30 1.35-1.65 0.30
JIS G4805 SUJ2 0.95-1.10 0.50 0.025 0.025 0.15-0.35 1.30-1.60
BS 970 535A99/EN31 0.95-1.10 0.40-0.70 0.10-0.35 1.20-1.60

People Also Search :

e52100 chemical composition e52100 steel bar e 52100 heat treat
e52100 alloy steel properties aisi e52100 equivalent e 52100 heat treatment
e52100 equivalent e52100 round bar e52100 steel hardness
e52100 alloy steel balls difference between e 52100 and 52100 e 52100 mechanical properties
e52100 steel material properties e52100 steel composition e52100 steel mil-s-7420
e 52100 bearing steel steel comp e52100 density of e52100
e52100 steel properties e52100 density e52100 properties
e52100 steel equivalent e52100 steel density aisi e52100 properties
e52100 material e52100 material equivalent bearing-quality e52100 alloy steel
e52100 alloy steel density e52100 speeds and feeds sae e52100
e52100 steel grade e52100 e52100 tubing
e52100 vs 52100 e52100 weldability e52100 tensile strength
e52100 alloy steel welding e52100 heat treating e52100 steel
e52100 alloy steel machinability e 52100 yield strength uns e52100
e52100 alloy steel magnetic aisi e52100 aisi e52100 uni 100c6
e52100 alloy steel corrosion aisi e52100 steel 52100 vs e52100 steel
e52100 steel balls    

There's a world of steel & metals, Click on the below articles to check out the differences & learn more.

Looking to buy Inconel 600 Tube? Alloy 600 Tube?

Check price of Inconel 600 Tube in India

Inconel 600 Tube